Description
MASTERTOP 1330 is a tough, durable, polyurethane deck coating system, which provides a seamless and protective, waterproof, wear resistant, smooth or skid-resistant surface.
The system comprises a unique combination of polymers which incorporates:
- MASTERTOP PRIMER 2 - Is a high grade, low-viscosity, two component epoxy resin coating for mineral surfaces. MASTERTOP PRIMER 2 is used as a sealer or a filler with and without the addition of quartz sand.
- Mastertop SRA No. 3 - A graded, high purity quartz aggregate with a particle size in the range 0.3 –0.9mm. Used as a multi action: mechanical key, wear enhancer and to provide skid resistance, it's use is the means by which thickness is attained with economy for the various wearing conditions such as: in traffic lanes, ramps and turning areas.
- MASTERTOP TOP COAT 40P - Is a one component PUR coating compound with a low solvent content suitable for, among other things, top seals in parking decks. It provides UV-resistant, hard-elastic surfaces which are resistant to chemicals and abrasion.
Primary uses
MASTERTOP 1330 may be specified as a waterproof and protective wear resistant membrane for a variety of applications including:
- Car park decks
- Trafficable flat roofs
- Ramps
- Plant rooms
- Stadia seating, bleachers
- Balconies
- Protects concrete from the damaging effects of salt water, de icing salts, chemicals, fuel and oil spillage.
- Non skid, decorative, crack bridging, easily maintained surface enhances durability of the substrate concrete.
Packaging
MASTERTOP 1330 is supplied in individual system components as follows:
- MASTERTOP PRIMER 2 - 12.4kg units
- MASTERTOP SRA No 3 - 25kg
- MASTERTOP TOP COAT 40P - 35kg units
Coverage
| MASTERTOP PRIMER 2 |
0.15-0.3kg/m² depending on surface texture and porosity. |
| MASTERTOP TOP COAT 40P |
0.3-0.8kg per m² per coat. Two coats minimum |
Thickness
1-2mm. Read the method statements for multi-layer systems.
Typical properties*
MASTERTOP PRIMER 2 - Typical properties
Cured at 7 days @20°C |
|
|
Pot Life: |
25°C |
20 mins |
Density: |
|
1.09 |
Bonding strength |
Greater than cohesive strength of typical good quality concrete substrate |
Application time |
approx. 20 mins. at approx. 25°C |
Application temperature |
10°C to 40°C substrate temp |
Recoatable after |
approx. 6 hours at 30°C |
| |
approx. 12 hours at 20°C |
| |
approx. 24 hours at 10°C |
MASTERTOP TOP COAT 40P - Typical properties
| Mixed density |
1.30-1.40gm/cm³ depending on colour |
| Curing at 20°C and 60% rel. atm. hum. |
Capable of bearing loads at 48 hours |
| |
tack free approx. 30 mins. |
| |
to be walked on approx. 2 hours |
| Reaction temperatures |
from +5°C to +40°C |
| Rel. atm. humidity |
40-90% |
| Tensile strength DIN 53504 |
approx. 4.5N/mm² |
| Breaking elongation DIN 53504 |
approx. 200% |
| Water vapour diffusion resistance factor DIN 52615 |
approx. 3000 |
| Fire classification |
Swiss Fire Class, Fume Class 1 Resistant to flying fire and heat radiation in accordance with DIN 4102-B2 |
Standards
Complies to ASTM C957 : 1993 when tested in accordance with:
ASTM C501 : 1990
ASTM C794 : 1993
Tensile tested to ASTM D412 after exposure in accordance with:
ASTM G53
ASTM B117
Guide to application
Preparation:
Remove laitance, weak or friable concrete and all contaminants that could affect the bond to the substrate.
Suitable preparation includes light grit blasting, surface grinding etc. Surface defects should be repaired using CONCRESIVE 2200 or other suitable repair compounds from the CONCRESIVE or EMACO range.
Priming:
Mix and apply MASTERTOP PRIMER 2 surface conditioner to the prepared dust free surface at approximately 0.15-0.3kg/m². Into the wet primer, scatter 0.5kg/m² SRA No. 3.
Note: If a smooth surface finish is required, omit the aggregate scatter.
Allow to dry.
Application
MASTERTOP TOP COAT 40P should be stirred before use to ensure uniformity of colour.
Apply by roller, trowel or airless spray to the primed tack free surface.
Apply at the rate of 0.3-0.8kg/m² per coat with a minimum of 0.6kg/m². MASTERTOP TOP COAT 40P can be applied as a single coat, or as a multi coat sandwich system incorporating aggregates to give a slip resistant finish. When applying as a top coat or part of a multi coat system, do not exceed the maximum overcoating times of the previous coating.
Do not apply when the humidity exceeds 90%. Ensure that the substrate temperature is 3°C higher than the dew point.
Chemical resistance
MASTERTOP TOP COAT 40P is resistant to acids and lyes of medium concentrations, mineral oil products and solvents. Contact your local BASF office for specific details.
Storage
Store under cover out of direct sunlight and protect from extremes of temperature. In tropical climates the product must be stored in an air conditioned environment.
Failure to comply with the recommended storage conditions may result in premature deterioration of the product or packaging. For specific storage advice consult BASF's Technical Services Department.
Safety precautions
For further information, a material safety data sheet is available to the specialist applicator.
Note
Field service, where provided, does not constitute supervisory responsibility. For additional information contact your local BASF representative.
BASF reserves the right to have the true cause of any difficulty determined by accepted test methods.