MASTERTOP 1710 

Description

MASTERTOP 1710 is a multi-component water based epoxy floor coating system, designed for continuous protection at application thicknesses between 0.5mm-1.5mm, dependent on traffic levels. MASTERTOP 1710 is formulated to produce a smooth, matt, non-slip finish, even in wet conditions. The system is water vapour permeable allowing its use on damp substrates, so may be used to coat ‘green’ concrete floors, which it will additionally help to cure and fully hydrate.

Primary uses

MASTERTOP 1710 has good wear and abrasion resistance and is suitable for use in many industrial applications. It can be used as a surface coating where a hygienic and matt appearance is required, and is especially suitable in food, beverage, and wet process industries.

It provides impermeable protection against common oils, greases, lubricants, aviation fuels or oils such as Skydrol. In addition it offers good general chemical resistance, but as in all corrosive situations, a full analysis of operating and exposure conditions is required, followed by reference to chemical resistance data to ensure product suitability.

MASTERTOP 1710 is used extensively in the following industries:

• Pharmaceutical and other medical laboratory situations.
• Food and beverage production.
• Car production facilities.
• Aircraft hangars and maintenance areas.
• Warehouses.
• Traffic decking - including pedestrian and light duty vehicles.

Advantages

• Good wear and abrasion resistance.
• Easily applied.
• Smooth matt finish; easily cleaned.
• Good general chemical resistance.
• Non-slip when wet.
• Can be applied to damp or green concrete.

Packaging

MASTERTOP 1710 is supplied in 25kg units.

Typical properties*

Guide to application

Remove all surface laitance, oil, grease or any defective concrete that will reduce the bond of the MASTERTOP 1710 to the substrate.

Surface irregularities must be ground down or filled out with CONCRESIVE 2200 or repair materials from the EMACO range.

A light etch giving the texture of medium grit sand paper is the ideal surface profile for the application of MASTERTOP 1710, this can be achieved by captive blasting, light grit blasting or high pressure water jetting.

After all preparation has been completed, ensure all dust is removed from the surface.

MASTERTOP 1710 may be applied to 'green' concrete which has been given a light brush finish.

Application:

Prior to application MASTERTOP 1710 should be stored under cover and protected from extremes of temperature which will cause inconsistent workability, finish and cure times for the mixed material. Ideally at least 24 hours before mixing, MASTERTOP 1710 should be conditioned at approximately 20°C.

Sealing:

All concrete surfaces to be overlaid with MASTERTOP 1710 can be saturated with clean water to reduce localised suction and reduce the incidence of pin holes. If the concrete substrate is very porous the saturated substrate should be sealed with a single coat of MASTERTOP 1700 resins without the addition of the aggregate.

Pour the base into reactor component and mix together for 1 minute or until all striations have disappeared. Apply the mixed material to the pre soaked substrate ensuring there is no standing water, at the rate of 6-8 m² / ltr using a medium or short hair roller. Allow the sealer to become completely tack free before overcoating with MASTERTOP 1710.

Mixing / application:

Pour the base into the reactor, add the colour pack and mix for 1 minute using a drill and spiral mixing head.

When all striations have disappeared and a uniform colour is obtained, add the MASTERTOP 1710 aggregate, whilst continuing to mix until it can be seen that the mixed material is lump free.

Application:

To achieve a smooth finish apply the MASTERTOP 1710 with a short hair roller or squeegee, as a single coat at a minimum thickness of 0.5mm.

For thickness greater than 0.5mm, apply by pin screed or serrated trowel.

The coating should be rolled with a spike roller as soon as possible after application to achieve a uniform finish. Rolling should continue until all air is released and a uniform colour is obtained.

Always wear spiked shoes when rolling the MASTERTOP 1710 with a spiked roller.

Maintenance

To keep the floor in pristine condition it should be treated with 2 or 3 coats of an acrylic emulsion polish with a metallic base.

Watchpoint

MASTERTOP 1710 is suitable for application to smooth surfaces only.

Yield

A 25Kg unit will yield 16.5 litres.

MASTERTOP 1700 Resin only will yield 10.7 litres.

Coverage as sealer will be in the range of 6-8m²/litre.

Equipment care

Remove uncured MASTERTOP 1710 from tools and equipment using water.

Storage

Store out of direct sunlight, clear of the ground on pallets protected from rainfall. Avoid excessive compaction and protect from extremes of temperatures. In tropical climates the product must be stored in an air conditioned environment.

Failure to comply with the recommended storage conditions may result in premature deterioration of the product or packaging. For specific storage advice consult BASF's Technical Services Department.

Safety precautions

Request and refer to printed MSDS.

Note

Field service, where provided, does not constitute supervisory responsibility. For additional information contact your local BASF representative.

BASF reserves the right to have the true cause of any difficulty determined by accepted test methods.